Dyed Twisted High Tenacity Polyester Yarn 3000D AA Grade For Knitting Fabric
Brief introduction:
We can supply high tenacity.low shrinkage,super low shrinkage,HLMS industrial polyester filament
yarn as well as adhesive activated yarn and colored yarn,etc.
50D-3000D(single yarn)
500D-3000D(twisted yarn)
4000D-8000D(doubled yarn)
Packing:packed in bobbins,and then put in cartons + pallets.
48bobbins/pallets=528kg;64 bobbins/pallets=704 kg
One 20’GP can hold about 10.5MT.
One 40’GP can hold about 21MT,
One 40’HC can hold about 24.6MT.
| 1.General high tenacity yarn(HT) |
| Linear density/filament | Breaking strength | Breaking tenacity | Break elongation | Hor air shrinkage |
| D | DTEX | N | KG | CN/DTEX | G/D | % | % |
| 500/96F | 550 | 46.2 | 4.7 | ≥8.1 | 9.0 | 13.5±2 | 7.0±1.5 |
| 1000/192F | 1100 | 92.4 | 9.4 | ≥8.1 | 9.0 | 13.5±2 | 7.0±1.5 |
| 1500/192F | 1670 | 138.6 | 14.1 | ≥8.1 | 9.0 | 13.5±2 | 7.0±1.5 |
| 2000/288F | 2200 | 184.8 | 18.9 | ≥8.1 | 9.0 | 13.5±2 | 7.0±1.5 |
| 3000/576F | 3300 | 277.2 | 28.3 | ≥8.1 | 9.0 | 13.5±2 | 7.0±1.5 |
| Oil content(%):0.6±3 |
| Hot shrinkage test condition:177°C,10min,0.05cn/dtex |
1.Main applications:
V-belt fabrics, hoisting belts,conveyor belt,fire hoses,hoses,tie down belts.box belts,fishing nets,polyester cords,cordage,geotextile,geogrid,tire cord fabrics,canvas.
| 2.High tenacity low shrinkage yarn |
| Linear density/filament | Break strength | Break tenacity | Break elonation | Hot air shrinkage |
| D | DTEX | N | KG | CN/DTEX | G/D | % | % |
| 500/96F | 550 | 40.8 | 4.2 | ≥7.1 | 8.0 | 23.0±2 | ≤4.0 |
| 1000/192F | 1100 | 81.6 | 8.2 | ≥7.1 | 8.0 | 23.0±2 | ≤4.0 |
| 1500/192F | 1670 | 122.4 | 12.5 | ≥7.1 | 8.0 | 23.0±2 | ≤4.0 |
| 2000/288F | 2200 | 163.2 | 16.7 | ≥7.1 | 8.0 | 23.0±2 | ≤4.0 |
| Oil content(%):0.6±0.3 |
| Hot shrinkage test condition:190°C,15min,0.01cn/dtex |
2.Main applications:
Coating fabric,canvas,automobile tarpaulin.air inflating material,Havelock,water-proof cloth,advertisement jetting paint fabrics,beach umbrella,construction fabrics and bag materials.
| 3.High tenacity super low shrinkage yarn(SLS) |
| Linear density/filament | Break strength | Break tenacity | Break elongation | Hor air shrinkage |
| D | DTEX | N | KG | CN/DTEX | G/D | | |
| 500/96F | 550 | 37.0 | 3.7 | ≥6.7 | 7.5 | 23.0±2 | ≤2.5 |
| 1000/192F | 1100 | 75.5 | 7.7 | ≥6.7 | 7.5 | 23.0±2 | ≤2.5 |
| 1500/192F | 1670 | 113.0 | 11.5 | ≥6.7 | 7.5 | 23.0±2 | ≤2.5 |
| 2000/288F | 2220 | 151.0 | 15.4 | ≥6.7 | 7.5 | 23.0±2 | ≤2.5 |
| Oil content:0.6±0.3 |
| Hot air shrinkage test condition:190°C.15min,0.01cn/dtex |
3.Main applications:
Coating fabrics,canvas,automobile tarpaulin,air inflating meterials,Havelock,water-proof cloth,advertisement jetting paint fabrics,beach umbrella,construction fabrics,filter fabrics and bag materials.
| 4.Adhesive activated yarn(AA) |
| Linear density/filament | Breaking strength | Break tenacity | Break elongation | Hot shrinkage |
| D | DTEX | N | kg | CN/DTEX | G/D | | |
| 500/96F | 550 | 45.3 | 4.6 | ≥8.0 | 8.8 | 16±1 | 5.0±1.0 |
| 1000/192F | 1100 | 90.6 | 9.2 | ≥8.0 | 8.8 | 16±1 | 5.0±1.0 |
| 1500/192F | 1670 | 136.0 | 13.8 | ≥8.0 | 8.8 | 16±1 | 5.0±1.0 |
| 2000/288F | 2200 | 181.2 | 18.5 | ≥8.0 | 8.8 | 16±1 | 5.0±1.0 |
| Oil content(%):≤0.65±0.3 |
| Hot air shrinkage test condition:177°C,10min,0.05CN/dtex |
4.Main applications:rubber reinforcements,belting fabrics,etc.